Research and improvement of production technology of high-manganese steel 110G13L for railway frogs

This article is devoted to the study of the processes of joint deoxidation and modification of high-manganese steel 110G13L in (Al + Ti) and (FS45A15 + Ti), when performing a series of laboratory experiments in a resistance furnace (Tamman furnace). As a result, the change in the modifier during the melting of steel 110G13L for railway frogs, impact strength, in the total content of (FeO) and (MnO) = 5.18%, is 230 J/cm3 (at 20 °C).