Reduction of emissions polyaromatic hydrocarbons and protection of anode probes against corrosion at formation of the secondary self-burning anode

It is suggested to use compressed unbaked brings of anode paste with milled aluminum and low quantity of binder for the tarry matter discharge reduction while secondary anode formation and corrosion-prof protection of anode spikes. The cylindrical brings were made with pressure equipment, the dimensions of some of them match grains in the near-spike anode paste. Small dimensions of brings allow machine load in near-spike holes with measuring pocket used in production process. It was suggested to use extruders for mass brings production. There was tested aluminum foil isolation of anode spikes.