Patterns of structure formation in lime composites with additive based on amorphous aluminosilicates

Introduction. One of the reasons for coating destruction enclosing structures is the formation of condensate at the boundary of the fence and the finishing layer. As a result of external impact and freezing of moisture in the pores of the plaster coating, a network of small cracks is formed, and it is also possible to peel off the finishing layer. To test this hypothesis, the facades of three different buildings were examined. It is established that all the studied plaster coatings are made on the basis of cement mortar. It is also known that lime mixture is used less often due to the lack of sufficient resistance to moisture. Therefore, there is a need to increase the resistance of coatings based on lime compositions. This can be achieved by introducing an alumosilicate-based modifying additive into it. Materials and methods. Liquid sodium glass, aluminum powder PAP-1 and distilled water were used for the synthesis of the additive. Slaked lime (pushonka) with an activity of 84% was used to prepare test samples. Fritsch particle sizer Analysette 22 was used to analyze the granulometric composition of the additive. Compressive strength was determined on the samples measuring 20x20x20 mm. A testing machine of the type "IR 5057-50" was used for the study of compressive strength of samples. The analysis of rheological properties was determined by the Shvedov-Bingham equation. To study the plastic strength (ultimate shear stress) of the finishing mixture, a conical plastometer KP-3 was used. The plastic viscosity of the composition was determined with a rotary viscometer BCH 3. Results and discussions. The synthesized additive is a light powder of light gray color with a bulk density of 0.55 ± 0.05 g/cm3. The synthesized additive revealed a high content of oxides Al2O3, SiO2, Na2O respectively, amounting to 51.03%, 36.36%, 11.89%. The additive consists of particles of 100.0-200.0 microns, which make up more than 20% of the total composition. The influence of an aluminosilicate additive on a lime binder on rheological properties was investigated, a slight increase in static shear stress was revealed, respectively, an increase in the percentage of the additive. The value of the dynamic shear stress increases significantly with an additive content of more than 10%. Conclusions. The regularities of hardening of a lime binder with a nanostructured additive based on amorphous aluminosilicates are established, and the optimal content of an aluminosilicate additive in the amount of 10% by weight of lime is determined.