Arsenic (III) selenide has been synthesized in organic medium by using metaarsenite and amorphous selenium. The synthesis was carried out at the temperature range of 433-443 °K, pH >10, during 2-8 hours. Resulting sediment is filtered, washed at first by 0.1 M of acetate acid solution, then by ethyl alcohol and dried at 353 °K. The chemical analysis of the sediment is made, thermal, X-ray phase analyses are carried out, and electron microscope images of microparticles are taken.
Селенид мышьяка (iii), arsenic (iii) selenide, sodium metaarsenite, selenium, thermal analysis, morphology, x-ray analysis
Короткий адрес: https://sciup.org/14111125
IDR: 14111125 | УДК: 546.19; | DOI: 10.5281/zenodo.60203
Синтез As2Se3 в органической среде
Селенид мышьяка (III) синтезировали в органической среде с использованием метаарсенита и аморфного селена. Синтез проводили в температурном интервале 433-443 °K, при pH >10, в течение 2-8 часов. Образовавшийся осадок отфильтровывали, промывали сначала с помощью 0,1 М раствора уксусной кислоты, потом этиловым спиртом и сушили при температуре 353 °К. Проводился химический, термический, рентгенофазовый анализ осадка. Изображения микрочастиц получены с помощью электронного микроскопа.
Список литературы Synthesis of As2Se3 in organic medium
- Панасюк Л. M. Тезисы докладов международного конгресса. для высокой чувствительности фотографии и фотонике. М., 1980. 318 с.
- Исаева A. И., Казакова Л. П., Лебедев Е. А., Мехтиева С. И., Ятленко И. И., Способ получения халькогенидных стеклообразных полупроводников на основе Se -As, А. п. №1512015, М., 1989.